410S Steel Coil
Descriptio
Formularium:
1.Standard: ASTM A240, JIS G4304, EN10088
2. Gradus: 200series& 300series& 400series
3. Crassitudo: 0.03mm - 6.0mm
4. Latitudo: 8mm-600mm
5. Longitudo: ut clientium petitionem
6. Superficies: 2D,2B, BA, Speculum confectum, N04, Hair Line, Matt metam, 6K, 8K
7.Technology: frigus instructa / frigus involutus / calidum advolvit
Materiae:
| Type | Gradus | Gradus | Chemical Component % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Other | |||
| Austenitic | 201 | SUS201 | ≤0.15 | 16.00-18.00 | 3.50-5.50 | 5.50－7.50 | ≤0.060 | ≤0.030 | - | ≤1.00 | - | ≤0.25 | - |
| 202 | SUS202 | ≤0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0.060 | ≤0.030 | ≤1.00 | - | ≤0.25 | . | ||
| 301 | 1.4310 | ≤0.15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | ≤0.10 | - | |
| 304 | 1.4301 | ≤0.07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304L | 1.4307 | ≤0.030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304H | 1.4948 | 0.04-0.10 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309 | 1.4828 | ≤0.20 | 22.00-24.00 | 12.00-1500 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309S | * | ≤0.08 | 22.00-24.00 | 12.00-1500 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 310 | 1.4842 | ≤0.25 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| 310S | * | ≤0.08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| 314 | 1.4841 | ≤0.25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1.4401 | ≤0.08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316L | 1.4404 | ≤0.030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316Ti | 1.4571 | ≤0.08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | 0.1 | Ti5(C+N)~0.70 | |
| 317 | * | ≤0.08 | 18.00-20.00 | 11.00-1500 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 317L | 1.4438 | ≤0.03 | 18.00-20.00 | 11.00-1500 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 321 | 1.4541 | ≤0.08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 | |
| 321H | * | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 | |
| 347 | 1.4550 | ≤0.08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Nb≥10*C%-1.10 | |
| 347H | 1.494 | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Nb≥10*C%-1.10 | |
| Duplex | 2205 | S32205 | ≤0.03 | 22.0-23.0 | 4.5-6.5 | ≤2.00 | ≤0.030 | ≤0.020 | 3.0-3.5 | ≤1.00 | - | 0.14-0.20 | |
| 2507 | S32750 | ≤0.03 | 24.0-26.0 | 6.0-8.0 | ≤1.20 | ≤0.035 | ≤0.020 | 3.0-5.0 | ≤0.80 | 0.5 | 0.24-0.32 | ||
| Ferrite | 409 | S40900 | ≤0.03 | 10.50-11.70 | 0.5 | ≤1.00 | ≤0.040 | ≤0.020 | - | ≤1.00 | - | ≤0.030 | Ti6(C+N)~0.50 Nb: 0.17 |
| 430 | 1Cr17 | ≤0.12 | 16.00-18.00 | - | ≤1.0 | ≤0.040 | ≤0.030 | - | ≤1.0 | - | - | - | |
| 444 | S44400 | ≤0.025 | 17.50-19.50 | 1 | ≤1.00 | ≤0.040 | ≤0.030 | 1.75-2.5 | ≤1.00 | - | 0.035 | Ti+Nb:0.2+4(C+N)~0.80 | |
| Martensite | 410 | 1Cr13 | 0.08-0.15 | 11.50-13.50 | 0.75 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0.080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 420 | 2Cr13 | ≥0.15 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0.26-0.35 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0.07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | 3.00-5.00 | - | Nb 0.15-0.45 |
| 631 | 17-7PH | ≤0.09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | ≤0.50 | - | Al 0.75-1.50 | |
| 632 | 15-5PH | ≤0.09 | 14.00-16.00 | 3.50-5.50 | ≤1.00 | ≤0.040 | ≤0.030 | 2.00-3.00 | ≤1.00 | 2.5-4.5 | - | Al 0.75-1.50 | |
Basic notitia
410s Steel Coil, cum bene corrosione resistentiae et machinabilitatis, generalis est propositi ferrum et ferramentum asciale.410S est genus ferri quod corrosio resistentiae et formabilitas 410 chalybe.410S emendare potest, chalybea vis alta est, quae amplius ex ferro resistentia corrosionis 410 potest emendare.Ponitur pro scapulis turbine et caliditate partium.
• Specifications: AISI 410s, ASTM 410s
• Finit: superficies Ba, superficies 2b, No.1 (cutis alba), superficies 2D, No.4 (frosted), HL (filum trahens), 8K superficies optimam superficiem qualitatem habent.
• Molendinum tolerantiae in crassitiem & planitiam applicat. Voca JM Steel si vis certae magnitudinis vel frumenti directionis indigere.
410S Proprium machinis technologiae
1D -- Superficies habet figuram grani discontinuam, etiam notam sicut superficiem nebulae.
Processus technologiae: calidum volubilem + furnum offa peening servantur + frigus volubile + furnum servantur.
2D - A colore albo leviter argenteo.
Processus technologiae: calidum volubilem + furnum offa peening servantur + frigus volubile + furnum servantur.
2B -- Argentum album cum meliori glosa et planitate quam superficies 2D.
Processus technologiae: calidum volubilem + furnum offa peening servantur + frigidum volubilem + furnum servantur + exstinguiendi et temperandi volubilem.
Ba.
Processus technologiae: calidum volubilem + furnum offa peening servantur + frigidum volubilem + furnum salsamentum + superficies expolitio + exstingui et temperans volubilis.
No.3 -- Glosa bone, grossum grani superficiem.
Processus technologiae: politio et temperantia volvens pro 2D vel 2B cum 100~ 120 materiae laesurae (JIS R6002).
No.
Processus processus: politio et temperantia volventia pro 2D vel 2B cum 150~ 180 materiae laesurae (JIS R6002).
HL - Striae argentei cum pilis.
Processus technologiae: 2D producta vel 2B producta cum granularitate materiae laesurae congruis ad superficiem poliendam granum laesurae continuum est.
MIRRO - Specular.
Processus technologiae: 2D producta vel 2B producta cum congruenti granularitate materiae stridoris et poliendi ad effectum speculi.